Mae aloi gwrthsefyll OhmAlloy145 yn cynnwys alwminiwm cromiwm haearn gyda gwrthedd uchel, gwrthedd isel, tymheredd gweithredu uchel, ymwrthedd ocsideiddio da ar dymheredd uchel, y tymheredd cymwys uchaf hyd at 1250 gradd. Gwrth-ocsidiad rhagorol a chryfder mecanyddol ar dymheredd uchel.
Defnyddir yr aloi yn bennaf mewn ffwrneisi trydan diwydiannol, cydrannau gwresogi trydan cartref a chydrannau offer isgoch pell.
| Cyfansoddiad arferol (%) | |||||||||
| C | P | S | Mn | Os | Cr | Ni | Al | Ab | Arall |
| Max | |||||||||
| 0.05 | 0.025 | 0.025 | 0.70 | Uchafswm 0.6 | 21.0~23.0 | Uchafswm 0.60 | 5.0~7.0 | Bal. | Nb 0.5 |
| Priodweddau Mecanyddol Nodweddiadol(1.0mm) | ||
| Cryfder cynnyrch | Cryfder Tynnol | Ymuniad |
| Mpa | Mpa | % |
| 550 | 725 | 22 |
| Priodweddau ffisegol nodweddiadol | |
| Dwysedd (g/cm3) | 7.10 |
| Gwrthedd trydanol ar 20 gradd (Ωmm2/m) | 1.45 |
| Cyfernod dargludedd ar 20 gradd (WmK) | 13 |
|
Cyfernod ehangu thermol |
|
|
Tymheredd |
Cyfernod Ehangu Thermol x10-6/ gradd |
|
20 gradd - 1000 gradd |
16 |
|
Cynhwysedd gwres penodol |
|
|
Tymheredd |
J/gK |
|
20 gradd |
0.49 |
|
ymdoddbwynt ( gradd ) |
1510 |
|
Uchafswm tymheredd gweithredu parhaus mewn aer (gradd) |
1350 |
|
Priodweddau magnetig |
anfagnetig |
| Ffactorau Tymheredd Gwrthedd Trydanol | ||||||
| 20 gradd | 100 gradd | 200 gradd | 300 gradd | 400 gradd | 500 gradd | 700 gradd |
| 1 | 0.997 | 0.996 | 0.994 | 0.991 | 0.990 | 0.990 |
| 800 gradd | 900 gradd | 1000 gradd | 1100 gradd | 1200 gradd | - | - |
| 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | - | - |
| Arddull y cyflenwad | |||
| Enw aloion | Math | Dimensiwn | |
| OhmAlloy109W | Gwifren | D= 0.03~8mm | |
| OhmAlloy109R | Rhuban | W= 0.4~40mm | T= 0.03~2.9mm |
| OhmAlloy109S | Llain | W= 8}~250mm | T= 0.1~3.0 |
| OhmAlloy109F | Ffoil | W= 6}~120mm | T= 0.003~0.1 |
| OhmAlloy109B | Bar | Dia= 8}~100mm | L= 50~1000 |
Arddangosfa
Lluniau Cwsmer
Tagiau poblogaidd: aloi fecral ocr21al6nb, Tsieina ocr21al6nb aloi fecral gweithgynhyrchwyr, cyflenwyr, ffatri
Fe allech Chi Hoffi Hefyd
Anfon ymchwiliad